3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at: or !functionalprint@fedia.io
There are CAD communities available at: !cad@lemmy.world or !freecad@lemmy.ml
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
Be respectful, especially when disagreeing. Everyone should feel welcome here.
No porn (NSFW prints are acceptable but must be marked NSFW)
No Ads / Spamming / Guerrilla Marketing
Do not create links to reddit
If you see an issue please flag it
No guns
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe/ may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
Moderation policy: Light, mostly invisible
Hey everyone,
I am currently recalibrating my printer after.not using it for a while. When doing a flow test I noticed these blobs forming in the middle of the circles.
AFAIK these are often caused by moistures in the filament. I already dried the filament at 50°C for a couple hours in the oven and the problem persists. So I guess I should simply get rid of the filament and open a new pack?
What's your assessment?
https://feddit.org/comment/9055184
Maybe something is wrong with the script generating these test prints, if you don't have any similar problems with normal prints?
In addition to the blobs in the middle of the circles, I think it looks overextruded/blobby every time it changes direction. E.g. if you look at the -20 sample, it looks generally underextruded as one would expect. Though it's also blobby around the edges, where the lines make a U-turn. Since the printer usually slows down at turns (unless your acceleration is set insanely high) this could be an indication that you're exceeding your hotends melting capacity, i.e. either temp is too low or speed is too high, so it would be interesting to know what you calibrated those values to. I don't think this is usually associated with random blobbing in the middle of the print, but could be worth checking just in case.