3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at: or !functionalprint@fedia.io
There are CAD communities available at: !cad@lemmy.world or !freecad@lemmy.ml
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
Be respectful, especially when disagreeing. Everyone should feel welcome here.
No porn (NSFW prints are acceptable but must be marked NSFW)
No Ads / Spamming / Guerrilla Marketing
Do not create links to reddit
If you see an issue please flag it
No guns
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe/ may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
Moderation policy: Light, mostly invisible
My buddy has a cold plunge and this filter started cracking. After looking at it you can tell it's definitely 3d printed (and well)
On the left you can see my first attempt. I just cut rectangular holes in CAD and it's pretty close but not pretty. Printed in PETG on a K1 Max
Is there a way to do this in the slicer instead? I played around with 0 walls and different infill types but that didn't work out
I hope you meant PLA. Printing in PVC is a hilariously bad idea unless you do it inside a lab grade fume extractor or something. There's a reason barely anyone makes PVC filament.
PVC releases chlorine when heated which is not only incredibly harmful for you, but will also oxidize with and corrode all the metal parts in your printer and probably eventually embrittle its plastic parts as well. This is also why you should not make bongs out of PVC.
I suspect they meant ABS given ASA is also in their reply. No idea how good either material would be in this application, I just don't think it's possible to print PVC.